| 1. | Chemical bath deposition of cdse thin films and its patterning
薄膜的制备及其图形化 |
| 2. | The reaction mechanism of chemical bath is been studied
对常规化学浴的反应机理进行了分析。 |
| 3. | Structural and optical properties of chemical bath deposited cds thin films for cds cdte solar cells
多晶薄膜的结构和光学性能 |
| 4. | And the chemical bath for deposition of sns thin films was constitute of triethanolamine sncl2 2h2o , nh4cl . nh4oh and triethanolamine
以三乙醇胺、硫代乙酰胺、氯化亚锡、氨水、氯化铵为反应物，采用常规化学浴制备sns薄膜。 |
| 5. | In this paper , three methods have been employed to deposit sns thin films . thin films of sns were prepared by the chemical bath deposition method
本文采用了多种方法制备sns薄膜，并根据样品检测结果对这些方法进行了对比分析。 |
| 6. | The reaction mechanism of chemical deposition was studied , and the optimum reaction condition was obtained . the deposition of sns thin films by chemical bath with ultrasonication was studied
在不同条件下制备样品，初步得到了制备sns薄膜的优化条件，并研究了超声辅助手段对薄膜品质的影响。 |
| 7. | It presented the deposition process of cds thin films by chemical bath deposition ( cbd ) and treatment after prepared . the initial growth rates dependence on experimental conditions were investigated
还介绍了cbd ( chemicalbathdeposition )法制备cds薄膜的方法、后期处理以及沉积条件与cds薄膜生长的关系。 |
| 8. | The mechanism of chemical bath deposition of cds thin films was theoretically analyzed , and then proposed a modification to its mechanism , which is based on the successive absorption and decomposition of inter mediate species
理论上分析和探讨了cbd - cds薄膜的生长机理，提出了基于中间络合物吸附与分解的机理理论。 |
| 9. | Some results obtained are as follows : ( 1 ) chemical bath deposition of cds thin films is usually based on the decomposition of the thiourea in alkaline solution containing a cadmium salt , and then cds precipitations were produced as thin films on the substrate
总结起来得到了下列一些结论： ( 1 ) cbd法制备cds薄膜是利用镉盐和硫脲在碱性溶液中进行络合分解反应，产生硫化镉沉积到衬底上，从而得到硫化镉薄膜。 |
| 10. | Sem results imply that the surface of thin films deposited by chemical bath method is correlate to the reaction conditions . surface of sns thin films deposited by chemical bath method are coarse than thin films deposited by chemical bath with ultrasonication method and successive ionic layer adsorption and reaction method
Sem结果显示用常规化学浴方法所制备的薄膜样品的表面形貌与反应条件有关，而用超声波辅助化学浴和连续离子反应法制备的薄膜样品的表面较之常规化学浴方法所得到的薄膜样品表面晶粒细小均匀，致密平整。 |